Features:
1.High solar-thermal conversion and low heat loss
2.Stable advanced coating up to 380 ℃
3.Long time warranty to 15 years
4.High level vacuum ensure operation under cold weather
Advanced solar selective coatings
Advanced solar selective coatings employ two patent technologies :
(1) double cermet film structure with the highest photothermal efficiency
(2) metal-Aluminum nitride cermet (M-AlN) materials deposited by a novel sputtering technology.
The typical film structure of M-AlN cermet selective surfaces
|
Models
|
Ф47×150
|
Ф58×180
|
|
Weight
|
1.35±0.12kg
|
2.29±0.18kg
|
|
Structure
|
All glass coaxial double-layer tubes
|
All glass coaxial double-layer tubes
|
|
Outer tube diameter
|
Ф47±0.7mm
|
Ф58±0.7mm
|
|
Inner tube diameter
|
Ф37±0.7mm
|
Ф47±0.7mm
|
|
Outer Tube thickness
|
1.6±0.15mm
|
1.8±0.15mm
|
|
Inner tube thickness
|
1.6±0.15mm
|
1.6±0.15mm
|
|
Tubes length
|
1542±4mm
|
1812±4mm
|
|
Material of coating
|
AlN/AIN-SS/Cu
|
AlN/AIN-SS/CU
|
|
Absorptance
|
0.94~0.96
|
0.94~0.96
|
|
Emittance
|
0.04~0.06
|
0.04~0.06
|
|
Vacuum
|
P≤5×10-3pa
|
P≤5×10-3pa
|
|
Transmittance of Outer Tube
|
0.91
|
0.91
|
|
Stagnation temperature (height)
|
270~300 ℃
|
270~300 ℃
|
|
Heat-loss coefficient
|
≤0.6w/ m2* ℃ )
|
≤0.6 w/ (m2* ℃ )
|
|
Bearing hailstone ability
|
hailstone diameterФ25mm
|
hailstone diameterФ25mm
|
|
Pressure-endure ability
|
1MPa
|
1MPa
|